Green composites based on thermoplastic starch reinforced with micro- and nano-cellulose by melt blending - A review.

Starch is a biodegradable biopolymer, a sustainable material that can replace conventional petrochemical-based plastics. However, starch has some limitations, as it must be processed by heating and treated mechanically with a plasticizer to become thermoplastic starch (TPS). Different variables such as mixing speeds, amount, and kind of plasticizers play a vital role in preparing TPS by melting. Despite this, the properties of the TPS are not comparable with those of traditional plastics. To overcome this limitation, microcellulose or nanocellulose is added to TPS by melt mixing, including the extrusion and internal mixing process, which enables large-scale production. This review aims to compile several studies that evaluate the effect of plasticizers, as well as the relevance of incorporating different cellulosic fillers of different dimensions on the properties of TPS obtained by melt mixing. Potential applications of these materials in food packaging, biomedical applications, and other opportunities are also described.

Mechanical and Antimicrobial Polyethylene Composites with CaO Nanoparticles.

Low-density polyethylene composites containing different sizes of calcium oxide (CaO) nanoparticles were obtained by melt mixing. The CaO nanoparticles were synthesized by either the sol-gel or sonication methods, obtaining two different sizes: ca. 55 nm and 25 nm. These nanoparticles were used either as-synthesized or were modified organically on the surface with oleic acid (Mod-CaO), at concentrations of 3, 5, and 10 wt% in the polymer. The Mod-CaO nanoparticles of 25 nm can act as nucleating agents, increasing the polymer's crystallinity. The Young's Modulus increased with the Mod-CaO nanoparticles, rendering higher reinforcement effects with an increase as high as 36%. The reduction in Escherichia coli bacteria in the nanocomposites increased with the amount of CaO nanoparticles, the size reduction, and the surface modification. The highest antimicrobial behavior was found in the composites with a Mod-CaO of 25 nm, presenting a reduction of 99.99%. This strong antimicrobial effect can be associated with the release of the Ca2+ from the composites, as studied for the composite with 10 wt% nanoparticles. The ion release was dependent on the size of the nanoparticles and their surface modification. These findings show that CaO nanoparticles are an excellent alternative as an antimicrobial filler in polymer nanocomposites to be applied for food packaging or medical devices.